| Technical Specifications: Bat Brand PVC S-1300 is mainly used in electrical insulation materials, films, artificial leather, plastic sandals, and plastic construction materials. |
| Specifications |
White powder |
| Grade A |
Grade B |
Standard Grade |
| Viscosity (ml/g) |
127～135 |
| # of foreign particles ≤ |
16 |
30 |
80 |
| Mass fraction of vaporized substance (including water)/％≤ |
0.30 |
0.40 |
0.50 |
| Apparent density (g/ml) ≥ |
0.45 |
0.42 |
0.40 |
| Remaining substance after sifting/% |
250μsieve pore ≤ |
2.0 |
2.0 |
8.0 |
| 63μsieve pore ≥ |
95 |
90 |
85 |
| # of “fisheye”/ 400cm2≤ |
20 |
40 |
90 |
| Plasticizer-absorbing ability per 100g resin/ g ≥ |
26 |
25 |
23 |
| White degree (160℃,10min) / ％≥ |
78 |
75 |
70 |
| Conductivity of aqueous extract /[μs/(cm.g)]≤ |
5 |
5 |
- |
| Content of remaining VCM /(μg/g)≤ |
5 |
10 |
30 |
PVC S-1000
| Technical Specifications:Bat Brand PVC S-1000 is mainly used for transparent materials, building materials, artificial leather and pipes. |
| Specifications |
White powder |
| Grade A |
Grade B |
Standard Grade |
| Viscosity (ml/g) |
107～118 |
| # of foreign particles ≤ |
16 |
30 |
80 |
| Mass fraction of vaporized substance (including water)/％≤ |
0.40 |
0.40 |
0.50 |
| Apparent density (g/ml) ≥ |
0.48 |
0.45 |
0.42 |
| Remaining substance after sifting/% |
250μsieve pore ≤ |
2.0 |
2.0 |
8.0 |
| 63μsieve pore ≥ |
95 |
90 |
85 |
| # of “fisheye”/ 400cm2≤ |
20 |
40 |
90 |
| Plasticizer-absorbing ability per 100g resin/ g ≥ |
19 |
17 |
- |
| White degree (160℃,10min) / ％≥ |
78 |
75 |
70 |
| Conductivity of aqueous extract /[μs/(cm.g)]≤ |
- |
- |
- |
| Content of remaining VCM /(μg/g)≤ |
5 |
10 |
30 |
PVC S-800
Technical Specifications:Bat Brand PVC S-800 is mainly used for pipes and pipe parts such as water supply pipes, drainage pipes, and other related materials.
Construction and Decoration materials: doors and window frames, lamp covers and shades, plastic cards, plastic boards, plastic sheets, plastic molds, |
| Specifications |
White powder |
| Grade A |
Grade B |
Standard Grade |
| Viscosity (ml/g) |
87～95 |
| # of foreign particles ≤ |
20 |
40 |
80 |
| Mass fraction of vaporized substance (including water)/％≤ |
0.40 |
0.40 |
0.50 |
| Apparent density (g/ml) ≥ |
0.50 |
0.45 |
0.42 |
| Remaining substance after sifting/% |
250μsieve pore ≤ |
2.0 |
2.0 |
8.0 |
| 63μsieve pore ≥ |
95 |
90 |
85 |
| # of “fisheye”/ 400cm2≤ |
30 |
50 |
90 |
| Plasticizer-absorbing ability per 100g resin/ g ≥ |
12 |
- |
- |
| White degree (160℃,10min) / ％≥ |
75 |
70 |
70 |
| Conductivity of aqueous extract /[μs/(cm.g)]≤ |
- |
- |
- |
| Content of remaining VCM /(μg/g)≤ |
5 |
10 |
30 |
|
|